S355K2H

S355K2H

S355K2H structural steel pipes are often used in structural and civil engineering, as well as in the construction sector. It is a low alloy high strength steel with good shape and impact toughness that is primarily used in the manufacture of bridges, ships, vehicles, boilers, high-pressure vessels, oil and gas pipelines, power station equipment, lifting transport institutions, large steel structures, and other similar items. Use it to replace regular carbon steel, considerably reducing the weight of the construction, and ensuring the use of dependable, long-lasting materials.

Numerous designations are assigned in accordance with EN 10210. For instance,

  • The symbol K in combination with either numerical i.e. 0 or 2, would mean that the specific impact properties of EN 10219 S355K2H Steel Pipeat specific temperature points of 0℃ and – 40℃ apiece.
  • The letter H is a designation intended for hollow sectioned products like the S355K2H Pipe.
  • The other designation that touches the base with regards to its application is the letter S, which is a typical feature of structural steel.

PRODUCT FEATURES

Designation for EN 10219 S355K2H sTEEL gRADE

  • The number of this European Standard (EN 10219 specification);
  • The capital letter S for structural steel;
  • The indication of the minimum specified yield strength for thickness ≤16mm is expressed in N/mm2;
  • The capital letters JR for the qualities with specified impact properties at room temperature;
  • The capital letter J and a number 0 or 2 for the qualities with specified impact properties at 0℃ and -20℃ respectively;
  • The capital letter H indicates hollow sections

Dimensions and Sizes of EN10219 S355K2H Pipe

NPS

O. D.

Nominal Wall Thickness

DN

Inch

mm

SCH5S

SCH10S

SCH10

SCH20

SCH30

SCH40

SCH60

SCH80

SCH100

SCH120

SCH140

SCH160

STD

XS

XXS

50

2″

60.3

1.65

2.77

3.91

5.54

8.74

3.91

5.54

11.07

65

2-1/2″

73

2.11

3.05

5.16

7.01

9.53

5.16

7.01

14.02

80

3″

88.9

2.11

3.05

5.49

7.62

11.13

5.49

7.52

15.24

90

3-1/2″

101.6

2.11

3.05

5.74

8.08

5.74

8.08

100

4″

114.3

2.11

3.05

6.02

8.58

11.13

13.49

6.02

8.56

17.12

125

5″

141.3

2.77

3.4

6.55

9.53

12.7

15.88

6.55

9.53

18.05

150

6″

168.3

2.77

3.4

7.11

10.97

14.27

18.26

7.11

10.97

21.95

200

8″

219.1

2.77

3.76

6.35

7.04

8.18

10.31

12.7

15.09

18.26

20.62

23.01

8.18

12.7

22.23

250

10″

273.1

3.4

4.19

6.35

7.8

9.27

12.7

15.09

18.26

21.44

25.4

28.58

9.27

12.7

25.4

300

12″

323.9

3.96

4.57

6.35

8.38

10.31

14.27

17.48

21.44

25.4

28.58

33.32

9.53

12.7

25.4

350

14″

355.5

3.96

4.78

6.35

7.92

9.53

11.13

15.09

19.05

23.83

27.79

31.75

35.71

9.53

12.7

400

16″

406.4

4.19

4.78

6.35

7.92

9.53

12.7

16.66

21.44

26.19

30.96

36.53

40.49

9.53

12.7

450

18″

457.2

4.19

4.78

6.35

7.92

11.13

14.27

19.05

23.83

39.36

34.93

39.67

45.24

500

20″

508

4.78

5.54

6.35

9.53

12.7

15.09

20.62

26.19

32.54

38.1

44.45

50.01

550

22″

558.8

4.78

5.54

6.35

9.53

12.7

22.23

28.58

34.93

41.28

47.63

53.98

600

24″

609.6

5.54

6.35

6.35

9.53

14.27

17.48

24.61

30.96

38.89

46.02

52.37

59.54

Weldability of EN 10219 S355K2H Pipe

This European standard only allows for the use of weldable steel. EN 1011-1 and EN 1011-2 specify the critical parameters for the welding of the products covered by this European standard.

While welding these materials, the primary worry is the development of cold cracking in the welded zone as the product’s thickness, strength level, and CEV grows. Cold cracking happens for a variety of reasons:

  • Enhanced diffusible hydrogen concentrations in the weld metal;
  • Brittle structure in the heat-affected zone;
  • High tensile stress concentrations in the welded joint

Chemical Composition % of Steel S355K2H (1.0576): EN 10219

Designation

Type of deoxidation

Sub Group

C

%

max.

Nominal thickness(mm)

Si

%

max.

Mn

%

max.

P

%

max.

S

%

max.

N

%

max.

According to EN10219

≤40

>40≤65

     

S355K2H

FF

QS

0.22

0.22

0.55

1.60

0.030

0.030

1)     The deoxidation methods are designated as follows:

FF-Full killed steel containing nitrogen binding elements in amounts sufficient to bind available nitrogen (e.g.min.0.020% total Al, or 0.015% soluble Al).

2)     QS-quality steel.

3)     It is permissible to exceed the specified values provided that for each increase of 0.001%N the P max content will be reduced by 0.005%, the N content of the ladle analysis, however, shall not be more than 0.012%

4)     The max. value for nitrogen does not apply if the chemical composition shows a minimum total Al content of0.020% with a minimum AL/N ratio of 2:1, or if sufficient other N-binding elements are present. The N-binding elements shall be recorded in Inspection Document.

Mechanical Properties for S355K2H Non-alloy Structural Steel

Steel Grade

Mechanical Properties

Impact Energy (KV J)

Yield Strength

 

Tensile Strength

 

Elongation

 

Test Temperature At Test Temperature of ℃

(Mpa)

(Mpa)

(%)

-20

0

20

S355K2H

355

510-680

22

40

Manufacturing Tolerances of EN 10219 S355K2H Pipe

Characteristic

Round Hollow Sections

Square and Rectangular Hollow Sections

Outside Dimension

± 1% with min ± 0.5mm and max ± 10mm

± 1% with min of ± 0.5mm

Thickness (T)

T≤5mm: ±10%

T≤5mm: ±10%

T>5mm: ± 0.5mm

T>5mm: ± 0.5mm

Out-of-Roundness

2%

Convexity

Max .8% with min 0.5mm

Squareness of side

90° ± 1°

External Corner Profile

T≤6mm: 1.6T to 2.4T

6<T≤10mm: 2.0T to 3.0T

T,10: 2.4T to 3.6T

Twist

2mm plus 0.5mm/m

Straightness

0.2% of total

0.15% of total

Mass

±6% on individual length

Inspection and Testing of EN 10219 S355K2H Hollow Sections

EN 10219 S355K2H is tensile tested according to EN 10002-1 and Charpy impact tested according to EN 10045-1.

Inspection or test type

Test frequency

Internal tests

Acceptance test

Mandatory

Chemical analysis

M

M

Tensile testing

M

One per tested batch

Dimension verification

M

M

Visual inspection

M

M

Optional

Flattening test or expansion test (option 18)

M

One per tested batch

Roughness testing

Not applicable

One per tested batch

NDT of the weld in order to identify any longitudinal discontinuities

Not applicable

Individual

NDT in order to detect any leaks

Marking of EN10219 S355K2H

Except as provided for in EN10219 10.2 for hollow sections which are bundled, each S355J0H section shall be marked by suitable and durable methods such as painting, stamping, adhesive labels, or attached tags with the following:

— the steel designation e.g., EN 10219-S355JOH;

— the manufacturer’s name or trademark;

— in the case of specific inspection: an identification number, e.g., order number, which permits the correlation of the product or delivery unit to the related document;

— the mark of the external inspection representative (where applicable).

 

When the items are provided bundled, the EN10219 10.1 marking must be on a label that is firmly affixed to the bundle.

Piling-pipe-supplied-by-Tianjin-United-Steel-Pipe
Piling Pipe
Hollow Section
show various kind of galvanized pipes
Galvanized Pipe
Steel Fabrication
Scroll to Top

Get A Quote Now

Fill in the form below and our team will be happy to assist you