EN 10219 S275J2H Steel tubes are hollow tubes for structural use.
Tensile strengths of Cold-Formed S275J2H Steel Welded Pipe range from 410Mpa to 580Mpa, with a minimum yield strength of 255Mpa. S275J2H tubes are widely used in civil engineering applications such as bridge building, structural frame construction, factory constructions, and mechanical engineering systems.
The symbol J and the letter 2 indicate that the quality has the required impact properties at -20°C, respectively.
Why choose tuspipe?
Since 1998, Tianjin United Steel Pipe Co., Ltd (TUSPIPE) has been committed to supplying high-quality line pipes.
With over 500,000 tons annual production capacity, the company serves various fields and industries, such as oil & gas exploitation and transmission, ship & auto-building, water & electricity, environmental protection, mechanical engineering, infrastructure construction and etc.
TUSPIPE places a premium on product quality and rigorous product quality control. In order to maintain good product quality, the company has established a Test & Inspection Center since 2004. With a series of state-of-the-art tests and inspection equipment, the test & inspection center is able to perform the tensile tests, hydro tests, impact tests, DWTT, etc.
Designation for EN 10219 S275J2H Steel Grade
- The number of this European Standard (EN 10219 specification);
- The capital letter S for structural steel;
- The indication of the minimum specified yield strength for thickness ≤16mm is expressed in N/mm2;
- The capital letters JR for the qualities with specified impact properties at room temperature;
- The capital letter J and a number 0 or 2 for the qualities with specified impact properties at 0℃ and -20℃ respectively;
- The capital letter H indicates hollow sections
Dimensions and Sizes of EN10219 S275J2H Pipe
DN | O. D. | W. T. | |||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Inch | mm | SCH5S | SCH10S | SCH10 | SCH20 | SCH30 | SCH40 | SCH60 | SCH80 | SCH100 | SCH120 | SCH140 | SCH160 | Sth | XS | XXS | |
50 | 2″ | 60.3 | 1.65 | 2.77 | – | – | – | 3.91 | – | 5.54 | – | – | – | 8.74 | 3.91 | 5.54 | 11.07 |
65 | 2 1/2″ | 73 | 2.11 | 3.05 | – | – | – | 5.16 | – | 7.01 | – | – | – | 9.53 | 5.16 | 7.01 | 14.02 |
80 | 3″ | 88.9 | 2.11 | 3.05 | – | – | – | 5.49 | – | 7.62 | – | – | – | 11.13 | 5.49 | 7.52 | 15.24 |
90 | 3 1/2″ | 101.6 | 2.11 | 3.05 | – | – | – | 5.74 | – | 8.08 | – | – | – | – | 5.74 | 8.08 | – |
100 | 4″ | 114.3 | 2.11 | 3.05 | – | – | – | 6.02 | – | 8.58 | – | 11.13 | – | 13.49 | 6.02 | 8.56 | 17.12 |
125 | 5″ | 141.3 | 2.77 | 3.4 | – | – | – | 6.55 | – | 9.53 | – | 12.7 | – | 15.88 | 6.55 | 9.53 | 18.05 |
150 | 6″ | 168.3 | 2.77 | 3.4 | – | – | – | 7.11 | – | 10.97 | – | 14.27 | – | 18.26 | 7.11 | 10.97 | 21.95 |
200 | 8″ | 219.1 | 2.77 | 3.76 | – | 6.35 | 7.04 | 8.18 | 10.31 | 12.7 | 15.09 | 18.26 | 20.62 | 23.01 | 8.18 | 12.7 | 22.23 |
250 | 10″ | 273.1 | 3.4 | 4.19 | – | 6.35 | 7.8 | 9.27 | 12.7 | 15.09 | 18.26 | 21.44 | 25.4 | 28.58 | 9.27 | 12.7 | 25.4 |
300 | 12″ | 323.9 | 3.96 | 4.57 | – | 6.35 | 8.38 | 10.31 | 14.27 | 17.48 | 21.44 | 25.4 | 28.58 | 33.32 | 9.53 | 12.7 | 25.4 |
350 | 14″ | 355.5 | 3.96 | 4.78 | 6.35 | 7.92 | 9.53 | 11.13 | 15.09 | 19.05 | 23.83 | 27.79 | 31.75 | 35.71 | 9.53 | 12.7 | – |
400 | 16″ | 406.4 | 4.19 | 4.78 | 6.35 | 7.92 | 9.53 | 12.7 | 16.66 | 21.44 | 26.19 | 30.96 | 36.53 | 40.49 | 9.53 | 12.7 | – |
450 | 18″ | 457.2 | 4.19 | 4.78 | 6.35 | 7.92 | 11.13 | 14.27 | 19.05 | 23.83 | 39.36 | 34.93 | 39.67 | 45.24 | – | – | – |
500 | 20″ | 508 | 4.78 | 5.54 | 6.35 | 9.53 | 12.7 | 15.09 | 20.62 | 26.19 | 32.54 | 38.1 | 44.45 | 50.01 | – | – | – |
550 | 22″ | 558.8 | 4.78 | 5.54 | 6.35 | 9.53 | 12.7 | – | 22.23 | 28.58 | 34.93 | 41.28 | 47.63 | 53.98 | – | – | – |
600 | 24″ | 609.6 | 5.54 | 6.35 | 6.35 | 9.53 | 14.27 | 17.48 | 24.61 | 30.96 | 38.89 | 46.02 | 52.37 | 59.54 | – | – | – |
Weldability of EN 10219 S275J2H Pipe
This European standard only allows for the use of weldable steel. EN 1011-1 and EN 1011-2 specify the critical parameters for the welding of the products covered by this European standard.
While welding these materials, the primary worry is the development of cold cracking in the welded zone as the product’s thickness, strength level, and CEV grows. Cold cracking happens for a variety of reasons:
- Enhanced diffusible hydrogen concentrations in the weld metal;
- Brittle structure in the heat-affected zone;
- High tensile stress concentrations in the welded joint
Chemical composition % of steel S275J2H (1.0138): EN 10219
Designation | Type of deoxidation | Sub Grop | C % max. Nominal thickness(mm) | Si % max. | Mn % max. | P % max. | S % max. | N % max. | ||
---|---|---|---|---|---|---|---|---|---|---|
According to EN10027-1 and lC 10 | According to EN10027-1 | ≤40 | >40≤65 | |||||||
S275J2H | 1.0138 | FF | QS | 0.2 | 0.22 | – | 1.5 | 0.035 | 0.035 | – |
1)The deoxidation methods are designated as follows: FF-Full killed steel containing nitrogen binding elements in amounts sufficient to bind available nitrogen (e.g.min.0.020% total Al, or 0.015% soluble Al). 2)QS-quality steel. 3)It is permissible to exceed the specified values provided that for each increase of 0.001%N the P max content will be reduced by 0.005%, the N content of the ladle analysis, however, shall not be more than 0.012% 4)The max. value for nitrogen does not apply if the chemical composition shows a minimum total Al content of0.020% with a minimum AL/N ratio of 2:1, or if sufficient other N-binding elements are present. The N-binding elements shall be recorded in lnspection Document. |
– S275J2H Maximum Carbon Equivalent Value (CEV) Based on Cast Analysis
Steel Grade | Maximum CEV for nominal thicknesses ≤40 mm % | |
---|---|---|
Steel Name | Steel Number | |
S275J2H | 1.0138 | 0,40 |
Mechanical Properties for S275J2H Non-alloy Structural Steel
Designation | Minimum Yield Strength REh in N/mm2 | Tensile Strength Rm in N/mm2 | Minimum Percentage Elongation L0-5,65√S0 | Impact Properties | ||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
According to EN10027-1 and lC 10 | According to EN10027-1 | Nominal thickness in mm | Nominal thickness in mm | Longitudinal | Transverse | Test Temperature | Minimum Average Absorbed Energy(J)for Standard test pieces | |||||
≤16 | >16≤40 | >40≤65 | <3 | ≥3≤65 | Nominal thickness in mm | |||||||
≤40 | >40≤65 | ≤40 | >40≤65 | |||||||||
S275J2H | 1.0138 | 275 | 265 | 255 | 430-580 | 410-560 | 22 | 21 | 20 | 19 | -20 | 27 |
Physical Properties of Steel Grade EN 10219 S275J2H
Temperature (°C) | Modulus of Elasticity (GPa) | Mean Coefficient of Thermal Expansion 10-6/(°C) between20(°C) and | Thermal Conductivity (W/m·℃) | Specific Thermal Capacity (J/kg·°C) | Specific Electrical Resistivity (Ωmm²/m) | Density (kg/dm³) | Poisson’s Coefficient. ν |
---|---|---|---|---|---|---|---|
44 | – | – | – | – | 0.23 | – | – |
664 | 857 | – | 23.3 | 413 | – | – | – |
516 | – | 14 | 14.2 | – | – | 132 | 321 |
Manufacturing Tolerances of EN 10219 S275J2H Pipe
Characteristic | Round Hollow Sections | Square and Rectangular Hollow Sections |
---|---|---|
Outside Dimension | ± 1% with min ± 0.5mm and max ± 10mm | ± 1% with min of ± 0.5mm |
Thickness (T) | T≤5mm: ±10% | T≤5mm: ±10% |
T>5mm: ± 0.5mm | T>5mm: ± 0.5mm | |
Out-of-Roundness | 2% | – |
Convexity | – | Max .8% with min 0.5mm |
Squareness of side | – | 90° ± 1° |
External Corner Profile | – | T≤6mm: 1.6T to 2.4T |
– | 6<T≤10mm: 2.0T to 3.0T | |
– | T,10: 2.4T to 3.6T | |
Twist | – | 2mm plus 0.5mm/m |
Straightness | 0.2% of total | 0.15% of total |
Mass | ±6% on individual length |
Inspection and Testing of EN 10219 S275J2H Hollow Sections of Non-alloy Steels
EN 10219 S275J2H is tensile tested according to EN 10002-1 and Charpy impact tested according to EN 10045-1.
Inspection Requirements | Inspection Frequency | |||
---|---|---|---|---|
Type of test | Non-specific inspection | Specific inspection | ||
Mandatory tests | 1 | Cast analysis | One result per delivery item | One per cast |
2 | Tensile test | One result per delivery item | One per test unit ( b) | |
3 | Impact test for Qualities J2 and K2 only | Not applicable | One set per test unit (b) | |
4 | Surface condition and dimensions | – | – | |
5 | NDT of the weld | Not applicable | All products, full length | |
Optional tests | 6 | Product analysis | Not applicable | One per test unit a |
7 | Cast analysis additional elements | Not applicable | See Option 1.2 | |
8 | Impact test for qualities JR and J0 | Not applicable | One set per test unit (b) | |
b – Longitudinal or transverse samples at the discretion of the manufacturer. |